powder coat Variety and Performance:
Include high light, matt, sediment ripples, art-type pattern and
anti-corrosion powder with different color. Good film tough, Strong
impact resistance, light color, excellent construction performance,
good anti-corrosion ability and excellent insulativity.
Powder coat Application:
Suitable for all kinds of inhouse or outdoor products such as
household appliances, instruments, meters medical devices,
automotive components, metal furniture, fitness equipment, indoor
decorative painting, etc., also apply to a variety of equipment,
pipes, pipe fittings and other requirements of corrosion coating.
Specifications
1)Good film tough,
2)Strong impact resistance,
3)light color, excellent constructio performance, good
anti-corrosion ability
4) automotive car paint
Application:
Suitable for all kinds of products such as household appliances,
instruments, meters medical devices,
automotive components, metal furniture, fitness equipment, indoor
decorative painting, etc.,
also apply to a variety of equipment, pipes, pipe fittings and
other requirements of corrosion coating.
Powder physical properties:
Specific gravity: 1.4-1.7 (for color and gloss vary)
Particle size distribution: 100% less than 100 microns (based on the special requirements of
coating adjusted)
Fluidity: 120-140
Inspection Item
| Test Standard or Method
| Test Indicator |
| Type A | Type B,C |
| Impact resistance | ISO6272 | GB/T1732-1993 | 40cm | 50cm |
| Cupping test | ISO1520 | GB/T9753-1988 | 5mm | 8mm |
| Adhesion(Planning grid method) | ISO2409 | GB/T9286-1998 | Grade 0 |
| Crook | ISO1519 | GB/T6742-1986 | 3mm | 2mm |
| Pencil hardness | ASTMD3363 | GB/T6739-1996 | 1H-2H |
| Salt test | ISO7253 | GB/T1771-1991 | > 500 hours |
| Heat test | ISO6270 | GB/T1740-1979 | > 1000 hours |
| Heat resistance | 100°C/24 hours (white) | Paul Light character (best) |
Remark
| 1, The above test use cold-rolled steel(thichness:0.8mm) to remove rust,oil. Film thickness: 50-70um. 2, All the indicators of film features will be down lightly
depending on reducing of luster. |