General introduction
This prepared from the epoxy resin,and it has excellent chemical
tesistandeand good mechanical properties .It is suiltable for the
coating of metsallic appliances that has regor demand on the
snti-corrosion,insulating propertees and flexbility.It is suggested
to usethis tupe of coating directly in the coating for outdoor
appliances.
Product Series
Standard and low temperature solidification type pouder coatings
can be provided.Products of different golss are
available,namely,high gloss(above80%),semi gloss950-80%),flat
floss(20-50%)and no gloss(below20%).
(The gloss can be abjusted according to the customers to the
demand)
Product Description
1, The product is non-toxic, does not contain solvents and does not
contain volatile toxic substances, so there is no toxic, no fire,
no "three wastes" emissions and otherpollution problems, in full
compliance with the requirements of the state environmental
protection law.
2, Raw material utilization rate is high, the powder can be
recycled, the utilization rate is over 99%.
3, Before being treated, a one-time construction, no base coating,
you can get enough thickness of the coating, easy to achieve
automated operation, high production efficiency, therefore it
reduces the cost.
4, Coating density, adhesion, impact strength and toughness are
good, the edge angle coverage rate is high, it has excellent
chemical resistance to chemical corrosion and electrical insulation
properties.
5, Powder coating is convenient for storage, transportation safety.
Anyang Star Powder Coating epoxy polyester and wood finish powder
coating
double epoxy anticorrosive iron oxide red pigment powder coating
| Edition of | 2012-02-16 | | |
| Type | Red pigment | | |
| Delivery Form | Powder | | |
| Chemical Class | Synthetic iron oxide alpha-Fe2O3 |
| Color Index | Pigment red 101(77491) |
| CAS No. | 1309-37-1 | | |
| Use Recommendation | Coating Industry | |
| | |
| | |
| COLOR VALUES AND TINTING STRENGTH | | |
| Reference | | | Standard: DIN 6174 |
| Min | Max | Test Method |
| Binder | Test Paste Based | |
| On R-05 | |
| |
| Full Shade | | | No.001, 2001-01-01 |
| L* | -0.7 | +0.7 | |
| a* | -0.7 | +0.7 | |
| b* | -0.7 | +0.7 | |
| E*ab | | 1.0 | |
| | | |
| | | |
| TECHNICAL DATA | | | |
| Min | Max | Test Method |
| Water-Soluble Content [%] | | 0.5 | DIN ISO787 Part 3 |
| Sieve Residue(0.045mm)[%] | | 0.1 | DIN 53195 |
| Fe2O3 [%] | 95.0 | | DIN 55913 Sheet 2 |
| Moisture (After Production) [%] | | 1.0 | DIN ISO787 Part 2 |
| Loss on Heating 1000℃1/2h [%] | | 5.0 | DIN 55913 Sheet 2 |
| Particle Shape | Spherical | Electron Micrographs |